Fourier Transform Infrared Spectroscopy and Scanning Electron Microscopy Characterization of Adhesive Produced From Polystyrene Waste

In this study, the optimized adhesive formulated from polystyrene waste was characterized for Fourier transform infrared (FTIR) spectra, Scanning Electron Microscopy (SEM) / Energy Dispersive X-ray (EDX) spectroscopy, solubility, density and water absorption for identification of existing functional group(s), morphology, elemental compositions, etc. The results revealed that polystyrene, unsaturated hydrocarbon has been degraded to form a new product containing aromatic compounds. SEM morphology showed well mixed blended adhesive with silver-like appearance due to additives and EDX revealed 12 existing elemental compositions with their corresponding percentage atomic weights as follows; carbon 93.14 %, hafnium 1.44 %, vanadium 1.66 %, chromium 1.40 %, bromine 0.47 %, palladium 0.26 %, copper 0.43 %, nickel 0.31 %, cobalt 0.29 %, potassium 0.38 %, iron 0.15 % and manganese 0.08 %. The produced polystyrene adhesive was sparsely soluble in water after 30 minutes; it has a density of 1041 kg/m3 and does not absorb moisture. Because of these results, the adhesive from polystyrene waste could serve as green adhesive, since there are no threats of toxic substance emission from the spectral analysis since most of the elements are used as a supplement in pharmaceuticals and catalyst in process industries.